410 Stainless Steel Bar

1. Standard: GB ASTM, JIS, etc

2. Grade: Type 410 Stainless Steel

3. Diameter: 2mm-300mm

4. Shape Manufactured: Flat Bar, Square Bar,
Round Bar,Hex Bar and special shapes.

5. Length: 2.00m-6.00m or as customers’ request

6. Surface finish: #4 polish, #6 polish, #7 polish, and #8 mirror finish

  • SPECIFICATION OF 410 STAINLESS STEEL BAR

    Alloy 410 Stainless Steel is the basic, general purpose martensitic stainless steel that is used for highly stressed parts and provides good corrosion resistance plus high strength and hardness. Alloy 410 contains a minimum of 11.5% chromium which is just sufficient enough to demonstrate corrosion resistance properties in mild atmospheres, steam, and many mild chemical environments. It is a general purpose grade that is often supplied in the hardened but still machineable condition for applications where high strength and moderate heat and corrosion resistance are required. Alloy 410 displays maximum corrosion resistance when it’s been hardened, tempered, and then polished.

    Yieh United Co. has the stainless steel bar products you need positioned in large depots to meet your demand. Yieh United Co. carries processed bars not only in different types, but also in various grades includes special free-machining grades, food industry-approved grades and materials includes low-sulfur material and dual-certified material.

    The normal stock of stainless bar is around 20,000 tons, which ensure the delivery time and flexible choice for our customers.

    Product Name Grade Size Finish Quote
    Stainless Steel Round Bar 410 Dia: 1.5mm-660mm Black & Pickled & Bright Get A Quote
    Stainless Steel Flat Bar 410 thickness: 3mm-25mm
    width: 12mm-305mm
    stock length: 2mm-10mm
    Black & Pickled & Bright Get A Quote
    Stainless Steel Square Bar 410 thickness:4mm-100mm (larger sizes available upon request) Black & Pickled & Bright Get A Quote
    Stainless Steel Hex bar 410 thickness:4mm -76mm (larger sizes available upon request) Cold rolled, bright surface, some
    need to do
    heattreatment properly according to customer’s
    request.
    Get A Quote
  • 410 STAINLESS STEEL BAR PROCESSING

    You can select a number of processing options to produce stainless steel bars to their exact specification, reducing material costs, production time, scrap and internal handling.

    Long Porduct Processing Service Overview
    Bar Cutting Thickness range is 1/16'' to 28'' diameter. Products cut include round bar, flat bar, hex bar, square bar, tubing and hollow bar, pipe, angles, channles, beams and tees,
    Bar Production Cutting Yieh United can provide production cutting for product diameter up to 4''. We utilize our production equipment to achieve these precision cuts with tight tolerances. All products can be cut to exact requirements.
    Bar Polishing Round bar, square bar, hex & flat bar, angles, other shapes including tubular products have OD & ID polishing available.
  • VALUE ADDED FOR 410 STAINLESS STEEL BAR

    • Polishing: can polish any stainless steel bar item to a #4 polish, #6 polish, #7 polish, or a #8 mirror finish. Stainless steel polished bar can also be cut to size.
    • Heatreating & Annealing: some grades of stainless steel bars can be heatreated to change the mechanical properties. Precipitation hardening stainless steel such as 17-4ph can be heattreated. 410 stainless steel bar can also be heatreated.
    • Multiple cutting stations allow us to ship cut stainless bar to size when you need it.
    • Grinding and polishing available upon request.
    • Special heat treat requirement can also be supplied.
    • Stainless round bars can also be polished or center-less ground to exact tolerance.
  • STANDARD CHEMICAL COMPOSITION

    Type C Mn Si P S Cr Ni
    410 max:0.15 max:1.00 max:1.00 max:0.04 max:0.03 min:11.5
    max:13.5
    max:0.5

    NOMINAL MECHANICAL PROPERTIES

    Grade Tensile Strength ksi (MPa) min Yield Strength 0.2% ksi offset ksi (MPa) min Elongation (% in 50mm) min Hardness (Brinell) MAX Hardness (Rockwell B) MAX
    410 65 (450) 30 (205) 20 217 96


    MECHANICAL PROPERTIES OF HEAT TREATED

    Heat Treatment T410 (0.14%C) Hardened 1800°F (982ºC)
    Rockwell Hardness 0.2& YS, ksi (MPa) UTS, ksi (MPa)
    Annealed* 81HRB 45.4 (313) 80.4 (554)
    Hardned & Tempered 400°F (204ºC) 43 HRC 156.1 (1076) 202.9 (1399)
    Hardned & Tempered 550°F (288ºC) 40 HRC 148.3 (1022) 187.0 (1289)
    Hardned & Tempered 600°F (316ºC) 40 HRC 148.8 (1026) 186.1 (1283)
    Hardned & Tempered 800°F (427ºC) 41 HRC 132.9 (916) 188.5 (1300)
    Hardned & Tempered 900°F (482ºC) 41 HRC 122.6 (845) 154.3 (1063)
    Hardned & Tempered 1000°F (538ºC) 35 HRC 127.9 (882) 154.3 (1063)
    Hardned & Tempered 1200°F (649ºC) 98 HRB 85.5 (589) 111.2 (767)

    NOMINAL PHYSICAL PROPERTIES

    Density lbm/in3 Thermal Conductivity BTU/hr-ft-°F Electrical Resistivity (in x 10-6) Modulus of Elasticity (psi x 106) Coefficient of Thermal Expansion (in/in)/°Fx106 Specific Heat (BTU/lb/°F) Melting Range (°F)
    at 68°F 14.4 at 212°F 56 at 68°F 29 5.90 at 68-392°F 0.11 at 68°F to 212°F 2700 to 2790
    0.276 6.5 at 68-1112°F