410 Stainless Steel Sheet/Plate

1. Thickness:0.1mm - 80mm
Width:800mm - 2,000mm
Length:300mm - 12,000mm

2. Surface:2B/HL/NO.4/8K
perforated,colored,checkered

3. Grades: Type 410 Stainless Steel

4. PVC film: Novacel(laser cutting)
Nitto(deep drawing)

5. Standard: ASTM/ASME UNS S41000

 

  • Alloy 410 Stainless Steel is the basic, general purpose martensitic stainless steel that is used for highly stressed parts and provides good corrosion resistance plus high strength and hardness. Alloy 410 contains a minimum of 11.5% chromium which is just sufficient enough to demonstrate corrosion resistance properties in mild atmospheres, steam, and many mild chemical environments. It is a general purpose grade that is often supplied in the hardened but still machineable condition for applications where high strength and moderate heat and corrosion resistance are required. Alloy 410 displays maximum corrosion resistance when it’s been hardened, tempered, and then polished.


    STANDARD CHEMICAL COMPOSITION

    Type C Mn Si P S Cr Ni
    410 max:0.15 max:1.00 max:1.00 max:0.04 max:0.03 min:11.5
    max:13.5
    max:0.5

     

    NOMINAL MECHANICAL PROPERTIES

    Grade Tensile Strength ksi (MPa) min Yield Strength 0.2% ksi offset ksi (MPa) min Elongation (% in 50mm) min Hardness (Brinell) MAX Hardness (Rockwell B) MAX
    410 65 (450) 30 (205) 20 217 96


    MECHANICAL PROPERTIES OF HEAT TREATED

    Heat Treatment T410 (0.14%C) Hardened 1800°F (982ºC)
    Rockwell Hardness 0.2& YS, ksi (MPa) UTS, ksi (MPa)
    Annealed* 81HRB 45.4 (313) 80.4 (554)
    Hardned & Tempered 400°F (204ºC) 43 HRC 156.1 (1076) 202.9 (1399)
    Hardned & Tempered 550°F (288ºC) 40 HRC 148.3 (1022) 187.0 (1289)
    Hardned & Tempered 600°F (316ºC) 40 HRC 148.8 (1026) 186.1 (1283)
    Hardned & Tempered 800°F (427ºC) 41 HRC 132.9 (916) 188.5 (1300)
    Hardned & Tempered 900°F (482ºC) 41 HRC 122.6 (845) 154.3 (1063)
    Hardned & Tempered 1000°F (538ºC) 35 HRC 127.9 (882) 154.3 (1063)
    Hardned & Tempered 1200°F (649ºC) 98 HRB 85.5 (589) 111.2 (767)

    NOMINAL PHYSICAL PROPERTIES

    Density lbm/in3 Thermal Conductivity BTU/hr-ft-°F Electrical Resistivity (in x 10-6) Modulus of Elasticity (psi x 106) Coefficient of Thermal Expansion (in/in)/°Fx106 Specific Heat (BTU/lb/°F) Melting Range (°F)
    at 68°F 14.4 at 212°F 56 at 68°F 29 5.90 at 68-392°F 0.11 at 68°F to 212°F 2700 to 2790
    0.276 6.5 at 68-1112°F

     

    APPLICATIONS OF 410 STAINLESS STEEL SHEET/PLATE

    • Cutlery
    • Steam and gas turbine blades
    • Kitchen utensils
    • Bolts, nuts, screws
    • Pump and valve parts and shafts
    • Mine ladder rugs
    • Dental and surgical instruments
    • Nozzles
    • Hardened steel balls and seats for oil well pumps
  • ADDITIONAL PROPERTIES OF 410 STAINLESS STEEL SHEET/PLATE

    • Corrosion Resistance
      >>Good corrosion resistance to atmospheric corrosion, potable water, and to mildly corrosive environments.
      >>Its exposure to everyday activities (sports, food preparation) is generally satisfactory when proper cleaning is performed after exposure to use.
      >>Good corrosion resistance to low concentrations of mild organic and mineral acids.
    • Welding Characteristics
      >>Readily welded by all standard methods.
      >>To reduce the risk of cracking, it is suggested to pre-heat the work piece to 350 to 400oF (177 to 204oC).
      >>Post weld annealing is recommended to retain maximum ductility.
    • Heat Treatment
      >>The proper hot work range is 2000 to 2200oF (1093 to 1204oC).
      >>Do not work this material below 1650oF (899oC).

  • SURFACE FINISH OF 410 STAINLESS STEEL SHEET/PLATE

    *Not all finishes are available in all alloys - (contact Yieh United Sales for more information)

    #1 Finish Hot rolled, annealed and pickled.
    #2D Finish A uniform, dull silver gray mill finish that is applied to thinner stainless steel coils,the thickness of which has been reduced by cold rolling.
    #2B Finish A semi polished surface achieved by finishing with the equivalent of a 80 to 120 grit abrasive. This finish has a pronounced grit line.
    #3 Finish A semi polished surface achieved by finishing with the equivalent of a 80 to 120 grit abrasive. This finish has a pronounced grit line.
    #4 Finish Also called brushed, directional or satin finish. A is characterized by fine polishing grit lines that are uniform and directional in appearance. The final abrasive used in the process is 150 to 220 grit.
    #4 Satin Brush Finish 150 to 180 grit finish A fine directional polish, typically used in the washroom accessories industry. Most 3.5″ floppy diskette cover plates have this finish.
    #6 Finish Polished finish achieved with the equivalent of a 240 grit abrasive. Finer grit lines and higher reflectivity than a No. 4 finish.
    #7 Finish Highly reflective surface obtained with the equivalent of a 320 grit abrasive. Minimal grit lines.
    No. 8 or True #8 mirror This is the most reflective mirror finish on the market. All of the polishing, or “grit,” lines from the preliminary polishing operations are removed. The look is that of a glass mirror. Sometimes referred to as a non directional mirror finish, Super 8, No. 9, Perfect No. 10, and even No. 12 mirror.
    CMP Super #8 mirror Chemical Mechanical Polished Super #8 mirror finished sheets are guaranteed to be free from any manufacturing defects. This product represents the ultimate in mirror polished stainless steel. It is available as a single-sided or double-sided mirror polished sheet.
    Hairline finish 80 – 140 grit finish A well defined directional polish. Starting base substrate is a No. 4 finish sheet; these sheets are polished to provide a “continuous long grain” hairline look. A finish which is popular with architects for its aesthetic, it is equally popular with fabricators due to it’s ease of fabrication and finish matching properties after welding operations.
  • INNOVATIVE TECHNOLOGY of 409 STAINLESS STEEL SHEET/PLATE

    At Yieh United Corporation, we never stop improving and developing our technologies to go beyond our customer’s expectations. We strive towards these goals to produce reliable products and ensure they can be fully utilized throughout their lifetime.

    stainless-steel-innovative-technology

  • PACKING FOR 410 STAINLESS STEEL SHEET/PLATE

    Our 410 stainless steel products are packed and labeled according to the regulations and customers’ requests.

    stainless-steel-sheet-standardpackageNote: This is Yieh United Corporation’s standard seaworthy packing for 410 stainless steel sheet sheet/plate.

    stainless-steel-sheet-special-packageNote: This is Yieh United Corporation’s special packing for 410 stainless steel sheet/plate (Extra fee is needed).

  • FAQ

    1. What is the minimum order quantity (MOQ)?
    - Normally, the MOQ for our stainless steel sheet is 200 Kg. If we have any excess inventory of stainless steel sheet, there’s no MOQ requirement. You can ask us to check when you are interested in purchasing them.

    2.What is the payment method?
    
- For new customers: 30%T/T deposit 70%T/T Before shipment.
– For partners and distributors, 30%T/T deposit 70% T/T Against B/L Copy.

    3.What is the acceptable currency?
    - We accept USD, EUR and RMB.

    4.What is the delivery time?
    
- 5 days in advance.

    5.Where is the loading port?
    - Normally, our loading ports are Shanghai, Tianjin, and Shenzhen. You can choose anyone of them, or you can select the other ports.

    6.What is the delivery term?
    - FOB, CIF, CFR, EXW

    7.Do you offer free samples?
    
- Yes, based on our stock status, we will send our customer free samples. The express fee is to be paid by our customers.

Inquiry Box

[contact-form-7 404 "Not Found"]

Search

Available Services

Services