410S Stainless Steel Sheet/Plate

1. Thickness:0.1mm - 80mm
Width:800mm - 2,000mm
Length:300mm - 12,000mm

2. Surface:2B/HL/NO.4/8K
perforated,colored,checkered

3. Grades: Type 410S Stainless Steel

4. PVC film: Novacel(laser cutting)
Nitto(deep drawing)

5. Standard: ASTM/ASME UNS S41008

  • Type 410S Stainless Steel is a non-hardening modification of Type 410. A small aluminum addition minimizes austenite formation at high temperatures, thereby restricting the alloy's ability to harden. The result is a soft, ductile condition when the material is rapidly cooled from above the critical temperature. This non-hardening characteristic also retards formation of hardening cracks when the steel is welded. The alloy is completely ferritic in the annealed condition.

     

    STANDARD CHEMICAL COMPOSITION

    Type C Mn Si P S Cr Ni
    410S max:0.08 max:1.00 max:1.00 max:0.04 max:0.03 min:11.5
    max:13.5
    max:0.60


    NOMINAL MECHANICAL PROPERTIES

    Grade Tensile Strength ksi (MPa) min Yield Strength 0.2% ksi offset ksi (MPa) min Elongation (% in 50mm) min Hardness (Brinell) MAX Hardness (Rockwell B) MAX
    410S 64.4(444) 42(290) 33 217 75


    NOMINAL PHYSICAL PROPERTIES

    Density lbm/in3 Thermal Conductivity BTU/hr-ft-°F Electrical Resistivity (in x 10-6) Modulus of Elasticity (psi x 106) Coefficient of Thermal Expansion (in/in)/°Fx106 Specific Heat (BTU/lb/°F) Melting Range (°F)
    at 68°F: 0.280 187 at 212°F 23.7 at 68°F 29 6.0 at 32-212°F 0.11 at 68°F to 212°F 2700 to 2790
    7.5 at 68-1200°F

     

    APPLICATIONS OF 410S STAINLESS STEEL SHEET/PLATE

    • Petroleum Refining and Petrochemical Processing
      >>Columns
      >>Distillation trays
      >>Heat exchangers
      >>Towers
    • Ore Processing
      >>Mining machinery
    • Thermal Processing
      >>Annealing boxes
      >>Partitions
      >>Quenching racks
    • Gate Valves
    • Press Plates
  • ADDITIONAL PROPERTIES OF 410S STAINLESS STEEL SHEET/PLATE

    • Oxidation Resistance
      >>Good oxidation resistance.
      >>Can be used in continuous service up to 1300°F (705°C).
      >>Scaling becomes excessive above 1500°F (811°C) in intermittent service.
    • Corrosion Resistance
      >>Corrosion resistance of 410S stainless steel is similar to type 410.
      >>Resists corrosion in atmospheric conditions, fresh water, mild organic and mineral acids, alkalis and some chemicals.
      >>Exposure to chlorides in everyday activities (e.g., food preparation, sports activities, etc.) is satisfactory when proper cleaning is performed after exposure to use.
    • Heat Treatment
      The alloy can not be hardened by heat treatment. It is annealed between 1600 - 1650°F (871- 899°C), and then air cooled to relieve cold working stresses. 410S should not be exposed to temperatures above 2000°F (1093°C), due to embrittlement. If large grains are found after annealing mildly cold-worked material, the annealing temperature should be decreased to 1200 - 1350°F (649 - 732°C).
    • Welding
      410S is generally considered to be weldable by the common fusion and resistance techniques. Special attention should be given to avoid brittle weld fractures during fabrication; this includes minimizing discontinuities, maintaining low weld heat input, and occasionally warming the part somewhat before forming. 410S is generally considered to have slightly poorer weldability than the most common ferritic stainless steel grade 409. A major difference can be attributed to the addition of alloy, to control hardening which results in the need for higher heat input during welding.

  • SURFACE FINISH OF 410S STAINLESS STEEL SHEET/PLATE

    *Not all finishes are available in all alloys - (contact Yieh United Sales for more information)

    #1 Finish Hot rolled, annealed and pickled.
    #2D Finish A uniform, dull silver gray mill finish that is applied to thinner stainless steel coils,the thickness of which has been reduced by cold rolling.
    #2B Finish A semi polished surface achieved by finishing with the equivalent of a 80 to 120 grit abrasive. This finish has a pronounced grit line.
    #3 Finish A semi polished surface achieved by finishing with the equivalent of a 80 to 120 grit abrasive. This finish has a pronounced grit line.
    #4 Finish Also called brushed, directional or satin finish. A is characterized by fine polishing grit lines that are uniform and directional in appearance. The final abrasive used in the process is 150 to 220 grit.
    #4 Satin Brush Finish 150 to 180 grit finish A fine directional polish, typically used in the washroom accessories industry. Most 3.5″ floppy diskette cover plates have this finish.
    #6 Finish Polished finish achieved with the equivalent of a 240 grit abrasive. Finer grit lines and higher reflectivity than a No. 4 finish.
    #7 Finish Highly reflective surface obtained with the equivalent of a 320 grit abrasive. Minimal grit lines.
    No. 8 or True #8 mirror This is the most reflective mirror finish on the market. All of the polishing, or “grit,” lines from the preliminary polishing operations are removed. The look is that of a glass mirror. Sometimes referred to as a non directional mirror finish, Super 8, No. 9, Perfect No. 10, and even No. 12 mirror.
    CMP Super #8 mirror Chemical Mechanical Polished Super #8 mirror finished sheets are guaranteed to be free from any manufacturing defects. This product represents the ultimate in mirror polished stainless steel. It is available as a single-sided or double-sided mirror polished sheet.
    Hairline finish 80 – 140 grit finish A well defined directional polish. Starting base substrate is a No. 4 finish sheet; these sheets are polished to provide a “continuous long grain” hairline look. A finish which is popular with architects for its aesthetic, it is equally popular with fabricators due to it’s ease of fabrication and finish matching properties after welding operations.
  • INNOVATIVE TECHNOLOGY of 410S STAINLESS STEEL SHEET/PLATE

    At Yieh United Corporation, we never stop improving and developing our technologies to go beyond our customer’s expectations. We strive towards these goals to produce reliable products and ensure they can be fully utilized throughout their lifetime.

    stainless-steel-innovative-technology

  • PACKING FOR 410S STAINLESS STEEL SHEET/PLATE

    Our 410S stainless steel products are packed and labeled according to the regulations and customers’ requests.

    stainless-steel-sheet-standardpackageNote: This is Yieh United Corporation’s standard seaworthy packing for 410S stainless steel sheet sheet/plate.

    stainless-steel-sheet-special-packageNote: This is Yieh United Corporation’s special packing for 410S stainless steel sheet/plate (Extra fee is needed).

  • FAQ

    1. What is the minimum order quantity (MOQ)?
    - Normally, the MOQ for our stainless steel sheet is 200 Kg. If we have any excess inventory of stainless steel sheet, there’s no MOQ requirement. You can ask us to check when you are interested in purchasing them.

    2.What is the payment method?
    
- For new customers: 30%T/T deposit 70%T/T Before shipment.
– For partners and distributors, 30%T/T deposit 70% T/T Against B/L Copy.

    3.What is the acceptable currency?
    - We accept USD, EUR and RMB.

    4.What is the delivery time?
    
- 5 days in advance.

    5.Where is the loading port?
    - Normally, our loading ports are Shanghai, Tianjin, and Shenzhen. You can choose anyone of them, or you can select the other ports.

    6.What is the delivery term?
    - FOB, CIF, CFR, EXW

    7.Do you offer free samples?
    
- Yes, based on our stock status, we will send our customer free samples. The express fee is to be paid by our customers.

Inquiry Box

[contact-form-7 404 "Not Found"]

 

 

Search

Available Services

Services